High-power UV laser has use in CFRP machining

Fast processing speeds without carbon fiber damage are possible

RAJESH PATEL, JAMES BOVATSEK, and MASAYUKI FUJITA

A strong drive to increase fuel efficiency and lower carbon emissions in transportation industries is driving the use of carbon fiber-reinforced polymer (CFRP) material in the fabrication of various aircraft and automobile parts. As the material's cost continues to decline, demand and use for it will further increase. CFRP is a lightweight, strong, and durable material with good corrosion and vibration resistance, making it a good candidate to replace many metal parts. An optimally designed CFRP part can be up to 70% lighter than steel and 30% lighter than aluminum—attributes that make CFRP attractive for use in many non-transportation-related industries such as components for wind energy production, sports equipment, oil exploration equipment, and consumer electronics products.

The attributes that make CFRP a unique and useful material also make it difficult to machine with high quality. Manufacturers using CFRP in their products are also looking to decrease fabrication costs. Conventional mechanical and abrasive waterjet cutting techniques are costly because of high tool wear and operating costs, and fiber fracture and delamination of material during machining is common and results in yield loss. The use of lasers for machining provides the advantages of a non-contact process and ease of automation in manufacturing environments. Laser machining eliminates tool wear and gradual degradation in quality associated with mechanical techniques, and reduces operating costs. Furthermore, fiber damage and delamination of material during machining can be reduced or eliminated. However, there is a key challenge for laser machining of CFRP, which is to machine it with both high throughput and with minimal heat-affected zone (HAZ) formation in the material.

Pulsed UV laser capabilities

High-power continuous-wave (CW) infrared (IR) wavelength lasers with multi-kilowatt power levels can machine CFRP at higher speeds, but leave the material with unacceptably large HAZ [1-3]. On the other hand, ultrafast lasers can provide low HAZ, but usually machine materials at slow speeds [4-6]. So, the challenge is to find a laser source and process that deliver a good balance of speed and quality. Pulsed nanosecond lasers have shown moderate processing speeds with reasonable quality, with the wavelength often having a significant impact on results achieved. In particular, stronger absorption at the ultraviolet (UV) wavelength results in good-quality machining. A laser such as Spectra-Physics' high-power Quasar UV laser with up to >60W UV and TimeShift pulse-shaping technology is uniquely suited to ablate, cut, and drill CFRP material without damaging the fibers, and deliver both high speed and quality.

To demonstrate the capability of the Quasar UV laser, we machined 250μm-thick polyacrylonitrile (PAN)-based CFRP plate material (FIGURE 1). We varied the pulse width, power, repetition rate, and scanning speed. We also tested the burst machining capability provided by Quasar's technology. The cutting speed and HAZ—here defined as the average length of exposed fibers along the cut line—were characterized for various conditions.

The Spectra-Physics logo cut in ~1mm-thick CFRP plate
FIGURE 1. The Spectra-Physics logo cut in ~1mm-thick CFRP plate.

Experimental results

Results show that both speed and quality are achieved with this laser. The smallest HAZ of ~15μm was achieved using 2ns pulses (FIGURE 2). This is an average over a number of process conditions, and in some cases the HAZ was effectively zero. Burst machining proved to be advantageous, achieving 20–50% higher cutting speeds for the same average power (FIGURE 3). Through additional process development and optimization efforts, we have shown that this laser can cut 250μm-thick CFRP plates at 70mm/s with HAZ of < 15μm (FIGURE 4).

The effect of pulse duration on HAZ
FIGURE 2. The effect of pulse duration on HAZ.

Besides cutting and drilling, bonding and joining of CFRP parts are very important processes since traditional riveting and other types of fastening techniques require drilling holes in the material, which can be detrimental to the strength of the part because of fiber damage during the drilling process. Thus, adhesive bonding is desirable and a commonly used technique for joining of CFRP parts. However, the parts need to be cleaned of various residues and debris imparted to the surface by the molding process. A thorough cleaning and surface texturing of the part without damaging the fibers is crucial to achieve higher joint strength.

The effect of power, repetition rate, and pulse duration (including burst of pulses) on cutting speed
FIGURE 3. The effect of power, repetition rate, and pulse duration (including burst of pulses) on cutting speed.

Painting of CFRP parts is also challenging because of low surface wettability and poor surface adhesion, both of which are improved with laser processing. A thorough laser cleaning and texturing of the surface is necessary prior to painting to improve wettability of the surface. Research shows that parts textured with a UV laser have higher lap shear strength compared to those textured with an IR laser [7]. Using the Quasar with >60W average power, we have demonstrated an area cleaning and surface texturing rate of 80mm2/min without any visible damage to the fiber (FIGURE 5).

A scanning electron microscopy (SEM) image of a CFRP sample showing excellent laser cut quality
FIGURE 4. A scanning electron microscopy (SEM) image of a CFRP sample showing excellent laser cut quality.

Conclusion

We demonstrate that pulsed UV nanosecond lasers are promising for CFRP processing. With the Quasar laser, the high power and programmable pulse width/shape result in both high quality and speed for CFRP processing, including cutting, drilling, surface texturing, and cleaning. With this high-power laser, we demonstrate that low HAZ without damaging the carbon fibers can be achieved with fast processing speeds. Further work is actively being pursued to extend to other configurations of processes and thicker materials, and to expand the study of the effect of laser parameters on machining CFRP.

Surface texturing and hole drilling in CFRP without any visible fiber damage using the Quasar UV laser
FIGURE 5. Surface texturing and hole drilling in CFRP without any visible fiber damage using the Quasar UV laser.

ACKNOWLEDGEMENTS

Quasar is a registered trademark of Spectra-Physics, and TimeShift is a trademark of Spectra-Physics.

REFERENCES

1. D. Herzog et al., "Laser cutting of CFRP using a 30 kW fiber laser," Proc. ICALEO, San Diego, CA (2014).

2. H. Hira and A. Tsuboi, "Study on cutting of CFRP plate by fiber laser," Proc. ICCM, Jeju Islan, Korea (2011).

3. F. Schneider, N. Wolf, and D. Petring, Phys. Procedia, 41, 415–420 (2013).

4. A. Wolynski, T. Herrmann, P. Mucha, H. Haloui, and J. L'huillier, Phys. Procedia, 12, 292–301 (2011).

5. R. Weber et al., "Heat accumulation in short-pulse laser processing of CFRP," Proc. ICALEO, Anaheim, CA (2012).

6. Y. C. Kim, O. Kim, S. W. Kim, and H. D. Kim, "Laser cutting of carbon fiber reinforced plastics (CFRP) by using femtosecond laser," Proc. LPM, Vilnius, Lithuania (2014).

7. F. Fischer, S. Kreling, and K. Dilger, "Surface pre-treatment of CFRP by using laser radiation, Proc. ICCM, 4792–4801 (2013).


RAJESH PATEL (raj.patel@spectra-physics.com), JAMES BOVATSEK, and MASAYUKI FUJITA are all with Spectra-Physics, Santa Clara, CA, www.spectra-physics.com.

Get All the Industrial Laser Solutions News Delivered to Your Inbox

Subscribe to Industrial Laser Solutions Magazine or email newsletter today at no cost and receive the latest news and information.

 Subscribe Now
ILS Blogs
David Belforte
David Beleforte

Let's grow LME

Mon Apr 22 08:51:00 CDT 2013

Looked at manufacturing lately?

Wed Mar 20 09:57:00 CDT 2013

Industrial laser market meets forecast

Fri Mar 08 10:59:00 CST 2013

Photonics West features ultra-fast and fiber lasers

Mon Feb 18 13:31:00 CST 2013

Follow us at Join us on

Twitter - Industrial Laser Solutions

PRESS RELEASES

Replacement lenses from II-VI Infrared eliminate need for beam centering

II-VI Infrared, the world leader in CO2 laser optics, is now providing replacement Trumpf Cut Len...

See Article Archive

View Industrial Laser Solutions past articles.

  •  
  •  
  •  
Copyright © 2007-2016. PennWell Corporation, Tulsa, OK. All Rights Reserved.PRIVACY POLICY | TERMS AND CONDITIONS